品名铁基合金粉产地河北铁含量≥55（%）
粒度80-150 150-300（目） 牌号铁粉包装规格桶
形状球形制作方法雾化法
铁基自熔性合金是铁——碳合金中加入一定量的硼、硅元素制成的，通常应用在常温——500℃以下耐磨损、耐弱酸腐蚀介质的机械零部件上，仅管铁基自熔性合金，综合性能不如镍、钴基合金，然而原料来源广泛，价格便宜，这是其得以普及应用的较大优势。下面介绍我公司铁基焊粉，建议用户在使用前应在120℃保温两小时低温烘烤后使用。
Iron-base fluxed alloy is produced by adding suitable amount of boron and silicon into iron-carbon alloy, which is usually used on the wearable and weak-acid-medium proofing accessories under 500℃. Although the performance of iron-base fluxed alloy can not match with that of the nickel or cobalt alloy, it has wide source materials and low prices, which is the great advantage for application. The following iron-base sprayed welding alloy powder should be dried by the customer under 120℃ for two hours before useing.型号规格(μm)特性简述主要用途物理性能应用工艺
Fe1-200/+100Fe1是奥氏体不锈钢型加入B、Si元素具有抗磨耐热、耐用腐蚀和抗热疲劳等综合性能。阀门密封面
热轧辊①HRC35-40
②熔点1250℃
③流动性17s/50g
④松装密度4.4g/cm3等离子堆焊
Fe2-200/+100同上同上阀门座①HRC38-44
②熔点1240℃
③同上
④同上
等离子堆焊
Fe5-200/+100
-106/+45Fe5是高铬铸铁型抗磨料磨损性极优，裂纹倾向大。石油钻杆接头,犁铧耙片等磨粒磨损工件①HRC62-67
②熔点1230℃
③流动性18s/50g
④松装密度4.5g/cm3等离子堆焊
氧乙炔 |